| Product | Solvent | Solid (%) | VISCOSITY (25°C, cps) | COLOR | OH VALUE (mgKOH/g) | HYDROXYL CONTENT (%) | Speciality | Application |
|---|---|---|---|---|---|---|---|---|
| DSU 1250 | TL/XYL | 50±2 | Z₄-Z₅ | <1 | 1-6 | 1.2 | Fast drying; CAB / NC compatibility; good aluminum powder arrangement; high hardness. | Aluminum powder paint and color paint for household appliance plastics. |
| DSU 4270A | BAC | 70±2 | Y-Z₃ | <1 | 5-9 | 4.2 | High gloss, fullness and chemical resistance. | Topcoat and varnish, tank topcoat. |
| HE6625T | XYL/BAC/PMA | 60 | 3,000-6,000 | <1 | 4-10 | 1.5 | Excellent aluminum powder arrangement; Good interlayer adhesion; Dry quickly. | It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for non-ferrous metal substrate coatings. |
| HE6628 | XYL/BAC/PMA | 60 | 3,500-7,000 | <1 | 2-6 | 0.9 | Excellent alignment of aluminum powder; Good adhesion to ABS, PS and metal substrates; Fast drying speed. | It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for PU plastic paint, hardware aluminum powder paint and pigmented coating. The coating can be sprayed on ABS and PS at one time. |
| HE6673 | BAC/XYL | 65 | 3,000-6,000 | <1 | 5-10 | 3.0 | High gloss, high fullness, good leveling property; Good weather resistance; Excellent chemical resistance. | It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for PU finish paint, automobile refinish paint and aluminum powder paint. |
| HE6775E | BAC | 70 | 4,000-8,000 | <1 | 6-12 | 3.0 | High gloss, high solid content, high fullness, good leveling property; Good weather resistance, fast drying. | It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for PU cover varnish, pigmented paint and motorcycle paint, home appliance cover varnish. |
| HE6790 | BAC | 70 | 2,000-7,000 | <1 | 5-9 | 4.5 | High fullness, high gloss; Fast drying, high hardness; Excellent chemical resistance. | It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It has a high fullness and high gloss appearance, excellent mechanical properties and chemical resistance, excellent aging resistance, and high construction solid content, especially suitable for automotive coatings and motorcycle coatings. |
| DSU 7027B | BAC | 70±2 | Z₁-Z₃ | <1 | 4-9 | 2.7 | High gloss, weatherability and fullness. | Automotive repairing paint, PU varnish. |
SOLVENT-BASED ACRYLIC POLYOL RESIN FOR PU
📞 Contact us for pricing:
Solvent-based acrylic polyol resin for PU is an acrylic resin dissolved in organic solvents, containing hydroxyl groups that react with isocyanates to form durable polyurethane coatings.